| 厂家(产地)：日本帝人 | 牌号：K-1300 | 销售方式：品牌经销 |
| 类型：标准料 |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 基本性能 | 比重 | ASTM D-792 | 1.20 | |||
| 物理性能 | 成型收缩率 | 流动方向 | ASTM D-955 | 0.5~0.7 | % | |
| 透光率 | 厚度3mm | ASTM D-1003 | 89 | % | ||
| 折射率 | ASTM D-542 | 1.585 | ||||
| 吸水率 | 23°C水中24小时 | ASTM D-570 | 0.20 | % | ||
| 成型收缩率 | 垂直方向 | ASTM D-955 | 0.5~0.7 | % | ||
| 机械性能 | 耐冲击强度值 | 艾氏、带缺口厚度3.2mm | ASTM D-256 | 930(95) | j/m(kgf· cm/cm) | |
| 拉伸模量 | ASTM D-638 | 2090(21300) | Mpa(kgf/cm2) | |||
| 负荷-挠曲温度 | 负荷0.451MPa(4.6kgf/cm) | ASTM D-648 | 146 | ℃ | ||
| 耐冲击强度值 | 艾氏、带缺口厚度6.4mm | ASTM D-256 | 160(16) | j/m(kgf· cm/cm) | ||
| 压缩强度 | ASTM D-695 | 75(760) | Mpa(kgf/cm2) | |||
| 负荷-挠曲温度 | 负荷-挠曲温度 | ASTM D-648 | 136 | ℃ | ||
| 拉伸率 | 屈服 | ASTM D-638 | 6 | |||
| 断裂 | ASTM D-638 | 130 | ||||
| 弯曲模量 | ASTM D-790 | 2190(22300) | Mpa(kgf/cm2) | |||
| 拉伸强度 | 屈服 | ASTM D-638 | 60(610) | Mpa(kgf/cm2) | ||
| 断裂 | ASTM D-638 | 84(860) | Mpa(kgf/cm2) | |||
| 洛氏硬度 | M标度 | ASTM D-785 | 77 | |||
| 弯曲强度 | ASTM D-790 | 87(890) | Mpa(kgf/cm2) | |||
| 电气性能 | 阻燃性 | 厚度1.47mm | UL 94 | 94V-2 | ||
| 介电率 | ASTM D-150 | 0.009 | 106Hz | |||
| 阻燃性 | 厚度3.05mm | UL 94 | 94V-2 | |||
| 耐电弧性 | ASTM D-495 | 110 | sec | |||
| 介电率 | 60Hz | ASTM D-150 | 2.95 | |||
| 体积电阻率 | ASTM D-257 | 3 | ×1016Ω.cm | |||
| 耐导电径迹性（CTI | IEC 112 | 300 | V | |||
| 绝缘破坏强度 | 快速加压值厚度1.6mm | ASTM D-149 | 30 | KV/mm | ||
| 热性能 | 温度指数 | 电学式 | 厚度1.47mm | UL 746B | 125 | ℃ |
| 冲击式 | 厚度1.47mm | UL 746B | 115 | ℃ | ||
| 非冲击式 | 厚度1.47mm | UL 746B | 125 | ℃ | ||
| 线膨胀系数 | 流动方向 | ASTM D-696 | 7 | ×10-5cm/cm/℃ | ||
| 线膨胀系数 | 垂直方向 | ASTM D-696 | 7 | ×10-5cm/cm/℃ | ||
运费说明
支持物流，快递和货运; 支持现金，银行转账. ★ 本公司原料低于1吨，不承担运费，订货1吨以上珠三角地区可送货上门; 省外客户物流，快递或货运; 不便之处敬请谅解，谢谢! ★ 选用物流或者快递的买家，请先确认当地是否有该物流或快递的营业网点。 ★ 原料到厂后，请不要拆外包装，应先仔细检查原料的外包装是否完好及原料型号是否与您所订购原料型号相匹配。 ★ 货物送达后，请时间检查，发现物流过程中出现大量包装损坏及原料外漏的,请让物流人员出具证明并保存，并在24小时内与我们联系。 ★ 如发货后未能及时收到，请及时与我们联系。 ★ 本公司原料售后的加工由客户负责，如需帮助，我公司工程部将竭尽所能与您共同协商处理。 ★ 本公司随货的基本资料包括《送货单》两联、《货款收据》一张，《商务经理名片》一张，如有其它需求，经双方协商而定！